PrimaCreator Value UV / DLP Resin Crystal Clear

  • When you want astonishing results for less cost than many other brands - PrimaCreator VALUE resin should be your first choice.

    • Less smell then many other resins
    • Easy to use
    • Crystal clear
    • Fast curing, between 4-8 seconds

2 in stock - Will be shipped the next day

Size
Color
Crystal Clear

    • When you want astonishing results for less cost than many other brands - PrimaCreator VALUE resin should be your first choice!

      Resin from our VALUE line is a high-quality resin made from the best materials. 
      Your prints cures in sunlight or a UV curing chamber. When the curing is finished, the result is a rock-hard print with very small shrinkage.
      When you go for the transparent resin you will have a crystal-clear transparency which is truly stunning. This resin does not get yellow when you cure it, it stays transparent.

      VALUE resin has many benefits over other brands of comparable resins.
      The most noticeable is that it doesn´t smell very much.
      VALUE resin is developed to perform well on low powered DLP machines such as the Wanhao Duplicator 7, SparkMaker Anycubic Photon, Zortrax Inkspire and other printers that uses UV light for curing.

      Optimized for UV Lightsource 395 – 405 nm.

      Fast curing time, 4 – 8 seconds per layer for quicker prints.
      After printing, clean you print in IPA (Isopropyl Alcohol) or resin cleaner to rinse of extra resin.

      When it's time for curing you can use sunlight or a uv curing chamber.
      Depending on print the curing times can vary:

      In a UV light curing chamber, it will take about 2-5 minutes.
      In sunlight, 10-20 minutes.
      In daylight on a cloudy day it can take up to 60 minutes.



      • Technical Specification  
        Flexural modulus:1166.81 Mpa ±10%   Elongation at break:28.406% ±10%
        Flexural strength:52.846  MPa ±10% Hardness(Shore D):85-87 D ±10%
        Viscosity:1000-1300 MPa·s Density:1.05—1.25 g/cm3
        Maximum pulling strength: 1954.9N ±10% Notched impact strength: 266.93 J/m ±10%
        Tensile strength:47.025 Mpa ±10% Absorb wavelength: 355-415nm
        Tensile Modulus: 561.781 Mpa±10%